Manufacturing method of colored glass

The invention discloses a manufacturing method of colored glass. The manufacturing method comprises the following specific steps: depositing a photonic crystal coating liquid on a substrate which does not change at 600 DEG C, depositing a ceramic precursor material after drying, sintering at 400-600 DEG C, coating a sintered product with glass powder or a glass powder dispersion liquid which can be molten at 500 DEG C or below, and heating and melting the glass powder. The color glass prepared by the method has the advantages of light transmittance, high strength and hardness, and photonic forbidden band structure color realized by the inverse opal structure. 本发明公开了彩色玻璃的制作方法。所述制作方法的具体步骤为：在600℃不发生变化的基板上沉积光子晶体涂布液，干燥后沉积陶瓷前驱体材料，400-600℃下烧结，在烧结产物上涂布可在500℃以下熔融的玻璃粉或玻璃粉分散液，加热熔融玻璃粉即得。此方法制备的彩色玻璃具有可透光性、较高的强度和硬度、以及通过反蛋白石结构实现的光子禁带结构色彩。