Preparation method of novel metal material

The invention discloses a preparation method of a novel metal material, which comprises the following steps: S1, material preparation: respectively grinding 50-80 parts of titanium, 30-40 parts of nickel, 10-15 parts of zinc oxide and 3-5 parts of tin into powder through a ball mill; s2, impurity removal is conducted, specifically, the prepared metal powder is washed with clean water, water is filtered out through filter paper, 1-15 parts of borax is added, and then drying is conducted in the environment of 200-600 DEG C; s3, smelting is conducted, specifically, a smelting furnace is preheated to 300-300 DEG C, and metal powder tin is added; after 2-5 min, the temperature is increased to 550-650 DEG C, and metal powder zinc is added; after 5-10 min, the temperature is increased to 1300-1500 DEG C, and metal powder nickel is added; after 10-15 min, the temperature is increased to 1700-1800 DEG C, and metal powder titanium is added; the mixed metal solution is vibrated through a vibrator at the frequency of 100