ADHESIVE SHEET AND LAMINATE MANUFACTURING METHOD

The present invention addresses the problem of providing an adhesive sheet provided concurrently with a step followability, durability, and handleability. The present invention relates to an adhesivesheet that has photo-crosslinkability, wherein the tensile stress at a tensile elongation of 2000% be...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	ITO MACHI, KURODA DAISUKE, SEGUCHI SEIJI, SHIMIZU JIRO, OSATO RYUYA
Format:	Patent
Sprache:	chi ; eng
Schlagworte:	ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE ADHESIVES CHEMISTRY DYES LAYERED PRODUCTS LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT ORNON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM METALLURGY MISCELLANEOUS APPLICATIONS OF MATERIALS MISCELLANEOUS COMPOSITIONS NATURAL RESINS NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL PAINTS PERFORMING OPERATIONS POLISHES TRANSPORTING USE OF MATERIALS AS ADHESIVES
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The present invention addresses the problem of providing an adhesive sheet provided concurrently with a step followability, durability, and handleability. The present invention relates to an adhesivesheet that has photo-crosslinkability, wherein the tensile stress at a tensile elongation of 2000% before photo-crosslinking is no more than 0.3 N/mm , the tensile modulus before photo-crosslinkingis 150 kPa to 300 kPa inclusive, and, when a is the tensile modulus before photo-crosslinking and b is the tensile modulus after photo-crosslinking, b/a is less than 3.0. 本发明的课题在于，提供兼具高度差追随性、耐久性及处理性的粘合片。本发明涉及一种粘合片，其为具有光交联性的粘合片，其中，所述粘合片的光交联前的拉伸伸长率2000％时的拉伸应力为0.3N/mm以下，光交联前的拉伸弹性模量为150kPa以上且300kPa以下，在将光交联前的拉伸弹性模量设为a、将光交联后的拉伸弹性模量设为b时，b/a小于3.0。