PRODUCTION OF GLASS FROM A MIXTURE COMPRISING CALCIUM OXIDE, AND GLASS FURNACE

The invention relates to a glass production method comprising the production of a glass precursor mixture for a glass furnace, in which water, sand and sodium carbonate are mixed in weight proportionsof between 0 and 5 %, 40 and 65 %, and greater than 0 and at most 25 % respectively, and, after at least 10 minutes, calcium oxide is added in a weight proportion of between 1 and 20 % of the total.The invention relates to a method for producing glass using a mixture containing, in particular, calcium oxide, and a glass melting furnace, said method and furnace using a burner with a flame directed at the glass batch. 本发明涉及一种玻璃生产方法，所述方法包括生产用于玻璃熔炉的玻璃前体混合物，其中水、沙子和碳酸钠分别以0至5％之间，40％至65％之间以及大于0且不超过25％的重量比例混合，并且在至少10分钟之后，以总量的1％至20％之间的重量比例添加氧化钙。本发明涉及用于使用特别是包含氧化钙的混合物来生产玻璃的方法，以及玻璃熔融熔炉，所述方法和熔炉使用具有指向玻璃批料的火焰的燃烧器。