Kaolin porcelain body and application method thereof

The invention relates to a kaolin porcelain body and an application method thereof. The kaolin porcelain body is characterized in that kaolin is used as a main raw material, tremolite, potash feldsparand fusion cakes are added as mineralizers, water and Xianshui are used as dispersion media, and ball milling, drying, granulating, aging, forming and firing are performed to obtain kaolin porcelain,wherein the kaolin is prepared by mixing calcined kaolin and raw kaolin according to certain proportions, the total mixing amount is 85-90wt%, the firing temperature range of the body is 1200-1370 DEG C, and the folding strength after firing can reach 80-140MPa. The kaolin porcelain body innovatively uses a big amount of kaolin (greater than 85wt%) in raw materials, fully utilizes the characteristics of wide firing range of the kaolin in a firing process as well as high strength and high stability of porzite formed by the kaolin in the traditional ceramic field, is of great importance in applying the kaolin in ceramic