Method for preparing Raney Ni/alpha-Al2O3 through Ni2Al3/alpha- Al2O3 etching

The invention discloses a method for preparing Raney Ni/alpha-Al2O3 through Ni2Al3/alpha-Al2O3 etching. The method comprises the following steps that commercially available NiO powder and Al powder are weighed according to a reaction formula that (6NiO+13Al) is equal to (3Ni2Al3+2Al2O3), and are mix...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Hauptverfasser:	JI GENSHUN, GUO TIEMING, GAO CHANGQI, JIA JIANGANG, MA QIN
Format:	Patent
Sprache:	chi ; eng
Schlagworte:	ALLOYS CHEMISTRY FERROUS OR NON-FERROUS ALLOYS MANUFACTURE OR TREATMENT OF NANOSTRUCTURES MEASUREMENT OR ANALYSIS OF NANOSTRUCTURES METALLURGY NANOTECHNOLOGY PERFORMING OPERATIONS SPECIFIC USES OR APPLICATIONS OF NANOSTRUCTURES TRANSPORTING TREATMENT OF ALLOYS OR NON-FERROUS METALS
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The invention discloses a method for preparing Raney Ni/alpha-Al2O3 through Ni2Al3/alpha-Al2O3 etching. The method comprises the following steps that commercially available NiO powder and Al powder are weighed according to a reaction formula that (6NiO+13Al) is equal to (3Ni2Al3+2Al2O3), and are mixed to react for 3 h; the mixed powder is placed in an SP-3 planetary ball mill to be mechanically ball-milled, wherein GCr15 is used as a grinding medium, the ball-to-powder mass ratio is 30:1, and the rotational speed of the SP-3 planetary ball mill is 400 r/min; and during the ball-milling process, the ball milling is stopped for 20 min after the mixed powder is ball-milled for 1 h, so that Ni2Al3/alpha-Al2O3 powder is obtained and taken out; and the obtained Ni2Al3/alpha-Al2O3 powder is corroded for 2 h with an NaOH solution with the weight percentage of 20%, and during the corrosion process, a reaction vessel is placed in a water bath of 70 DEG C. The Ni2Al3/alpha-Al2O3 powder is first prepared through mechanic