Preparation method of super absorbent compound fabric

The invention relates to the field of gel high polymer materials, and in particular relates to a preparation method of weather-resisting super absorbent resin compound fabrics. The preparation method comprises the following steps: step 1. washing and drying a fabric material needing to be compounded with water-absorbent resins; step 2. soaking the fabric material subjected to washing and drying in a polymerization reaction stock solution for 1-60 minutes; step 3. taking out the soaked fabric and removing abundant liquid through rolling, arranging in a drying oven or a drying tunnel at the temperature of 50 DEG or 90 DEG C, carrying out prepolymerization reaction for 0.5-2 hours; and step 4. arranging the fabric subjected to prepolymerization reaction into a drying oven or a drying tunnel at the temperature of 100-150 DEG C for carrying out crosslinking and drying for 20-80min, so as to obtain the super absorbent compound fabric. The preparation method belongs to a water-absorbing and moisture-absorbing materi