A METHOD FOR PRODUCING SPHEROIDIZED OR NON-LAMELLAR MICROSTRUCTURE STEELS

The present disclosure discloses a method for producing high strength hot rolled steel. The method includes casting a steel slab of a composition, comprising in weight%: carbon (C) of about 0.45 wt.% ? 1.2 wt.%, manganese (Mn) of about 0.0 -1.0 wt.%, silicon (Si) of about 0.0-0.5 wt.%, niobium (Nb) up-to 0.03 wt.%, sulphur (S) up-to 0.05 wt.% of S, phosphorous (P) up-to 0.05 wt.%, nitrogen (N) 0.002 wt.% - 0.012 wt.% and balance being Iron (Fe) optionally along with incidental elements. The method also involves, heating, hot rolling, cooling, coiling the steel and retaining the steel at an ambient temperature to produce high strength hot rolled steel with 75 - 95% spheroid microstructure and 5 - 25% pearlite microstructure. La présente divulgation concerne un procédé de production d'acier laminé à chaud à haute résistance. Le procédé comprend le coulage d'une brame d'acier ayant une composition comprenant en % en poids : du carbone (C) à hauteur d'environ 0,45 % en poids à 1,2 % en poids, du manganèse (Mn) à hauteur d'environ 0,0 à 1,0 % en poids, du silicium (Si) à hauteur d'environ 0,0 à 0,5 % en poids, du niobium (Nb) jusqu'à 0,03 % en poids, du soufre (S) jusqu'à 0,05 % en poids de S, du phosphore (P) jusqu'à 0,05 % en poids, de l'azote (N) à hauteur de 0,002 % en poids à 0,012 % en poids, et le reste étant du fer (Fe) éventuellement conjointement avec des éléments accessoires. Le procédé comprend également le chauffage, le laminage à chaud, le refroidissement, l'enroulement de l'acier et le maintien de l'acier à une température ambiante pour produire de l'acier laminé à chaud à haute résistance ayant une microstructure sphéroïde de 75 à 95 % et une microstructure de 5 à 25 % de perlite.