METHODS FOR PREPARING MICROCAPILLARY CARBON MOLECULAR SIEVE MEMBRANES

A process for preparing a microcapillary carbon molecular sieve membrane may include extruding a polyvinylidene chloride polymer to a thickness from 10 ?m to 1,000 ?m to form an extruded polymeric microcapillary film, wherein the extruded polymeric microcapillary film comprises a first end, a second end, and one or more microcapillaries extending from the first end to the second end; pre-treating the extruded polymeric microcapillary film at a temperature from 100 °C to 200 °C for a time from 1 hour to 48 hours to form a pre-treated polymeric microcapillary film; and pyrolizing the pre-treated polymeric microcapillary film at a temperature from 200 °C to 1,500 °C for a time from 15 minutes to 5 hours to form the microcapillary carbon molecular sieve membrane. Un procédé de préparation d'une membrane de tamis moléculaire de carbone microcapillaire peut comprendre l'extrusion d'un polymère de chlorure de polyvinylidène à une épaisseur de 10 µm à 1 000 µm pour former un film microcapillaire polymère extrudé, le film microcapillaire polymère extrudé comprenant une première extrémité, une seconde extrémité et un ou plusieurs microcapillaires s'étendant de la première extrémité à la seconde extrémité ; le prétraitement du film microcapillaire polymère extrudé à une température de 100 °C à 200 °C pendant une durée de 1 heure à 48 heures pour former un film microcapillaire polymère prétraité ; et la pyrolyse du film microcapillaire polymère prétraité à une température de 200 °C à 1 500 °C pendant une durée de 15 minutes à 5 heures pour former la membrane de tamis moléculaire de carbone microcapillaire.