CARBON MATERIAL FOR CATALYST CARRIER OF POLYMER ELECTROLYTE FUEL CELL, AND METHOD OF PRODUCING THE SAME

A carbon material for a catalyst carrier of a solid polymer fuel cell, the carbon material being a porous carbon material having a three-dimensional tree-shaped structure branched three-dimensionally, wherein the branch diameter is 81 mm or below and the following conditions are satisfied at the same time: (A) the BET specific surface area SBET is 400-1500 m2/g; and (B) in the relationship between the mercury pressure PHg and the mercury absorption amount VHg measured by mercury porosimetry, the amount of increase ?VHg:4.3-4.8 in the mercury absorption amount VHg measured when the common logarithm LogPHg of the mercury pressure PHg increases from 4.3 to 4.8 is 0.82-1.5 cc/g. In addition, a method for manufacturing such a carbon material for a catalyst carrier. L'invention concerne un matériau carboné destiné à un support catalytique d'une pile à combustible à polymère solide, le matériau carboné étant un matériau carboné poreux ayant une structure tridimensionnelle en forme d'arbre ramifié en trois dimensions, le diamètre de branche étant de 81 mm ou moins et les conditions suivantes étant satisfaites en même temps : (A) la surface spécifique BET SBET va de 400 à 1500 m2/g ; et (B) dans la relation entre la pression de mercure PHg et la quantité d'absorption de mercure VHg mesurée par porosimétrie au mercure, la quantité d'augmentation ?VHg:4,3-4,8 dans la quantité d'absorption de mercure VHg mesurée lorsque le logarithme décimal LogPHg de la pression de mercure PHg augmente de 4,3 à 4,8 est de 0,82 à 1,5 cc/g. L'invention concerne en outre un procédé permettant de fabriquer un tel matériau carboné destiné à un support catalytique.