TUNABLE ADSORBENTS

The present invention relates to a method for modifying the crystalline inorganic framework of an adsorbent with coatings to provide rate selectivity for one gas over others is described. The method described herein narrows the effective pore size of crystalline porous solids with pores less than about 5 A for rate selective separations. This method of the invention comprises treating the hydrated or partially hydrated zeolite with a silicone derived binding agent followed by subsequent heat treatment. The additive content and treatment are adjusted to match effective pore size to specific separations. The superior adsorbent has the added convenience of bead forming simultaneously with pore modification as well as having the treatment result in the yielding of high crush strength products. La présente invention concerne un procédé pour modifier la structure inorganique cristalline d'un adsorbant avec des revêtements afin de produire une sélectivité de débit pour un gaz par rapport à d'autres. Le procédé selon l'invention rétrécit la taille de pore effective de solides poreux cristallins ayant des pores inférieurs à environ 5 A pour des séparations sélectives de taux. Le procédé selon l'invention comprend le traitement de la zéolite hydratée ou partiellement hydratée avec un agent de liaison dérivé de la silicone suivi d'un traitement thermique ultérieur. La teneur en additif et le traitement sont ajustés afin de correspondre à une taille de pore effective pour des séparations spécifiques. L'adsorbant supérieur présente l'avantage pratique supplémentaire de la formation de billes simultanément avec la modification des pores, ainsi qu'un résultat de traitement dans la production de produits à haute résistance à l'écrasement.