MODIFIED POLYOLEFIN RESIN FOR ADHESION TO LOW-POLARITY BASE MATERIALS

The present invention provides a modified polyolefin resin that can form a coating that exhibits excellent adhesion to a low-polarity base material, especially a poorly adherable polyolefin base material with no surface treatment even when being dried at low temperatures and has flexibility (bendability). Provided is a modified polyolefin resin that is a modified product of a polyolefin resin having a melting point (Tm) by a differential scanning calorimeter (DSC) of 60 to 165°C with a modifier comprising the following (A): (A) a monomer mixture comprising Monomer Group (A-1) and Monomer Group (A-2) with a weight ratio of Monomer Group (A-1) to Monomer Group (A-2) ((A-1)/(A-2)) of 30/70 to 50/50. L'invention concerne une résine polyoléfinique modifiée qui permet de former un film de revêtement présentant une souplesse (flexibilité) ainsi qu'une excellente adhérence sur un substrat de faible polarité, en particulier un substrat polyoléfinique à surface non traitée sur lequel l'adhérence est difficile, même lorsqu'il est séché à basse température. L'invention concerne une résine polyoléfinique modifiée obtenue à l'aide d'un agent de modification qui contient (A) ci-dessous pour modifier une résine polyoléfinique présentant un point de fusion (Tm) de 60-165°C, tel que mesuré par calorimétrie différentielle à balayage (DSC). (A) Un mélange de monomères qui contient un groupe de monomères (A-1) et un groupe de monomères (A-2), le rapport pondéral ((A-1)/(A-2)) de groupe de monomères (A-1) au groupe de monomères (A-2) étant de 30/70 à 50/50.