COMPOSITION COMPRISING SEMI-CRYSTALLINE POLYOLEFIN AND SULFONYL-AZIDE, RESULTING FOAMS AND METHODS OF MAKING THE SAME

A foamable composition includes a semi-crystalline polyolefin having a crystallinity of at least 50% and a poly(sulfonyl azide) of at least 500 ppm based on the total weight of the foamable composition. The foamable composition has a melt strength of at least 20 cN, a melt drawability of at least 100 mm/s, flexural modulus is greater than about 240,000 psi. Such a composition can be used to make a low density foam having a density in the range from 0.005 g/cm3 to 0.6 g/cm3. A resulting foam or a fabricated article, the methods of the composition and the foam are also provided. La présente invention concerne une composition expansible comprenant une polyoléfine semi-cristalline ayant une cristallinité d'au moins 50 % et un poly (sulfonyl azide) d'au moins 500 ppm sur la base du poids total de la composition expansible. La composition expansible a une résistance à la fusion d'au moins 20 cN, une aptitude à l'emboutissage à l'état fondu d'au moins 100 mm/s, un module d'élasticité en flexion supérieur à environ 240 000 psi. Une telle composition peut être utilisé pour fabriquer une mousse à faible densité ayant une densité dans la plage de 0,005 g/cm3 à 0,6 g/cm3. L'invention concerne également une mousse ou un article fabriqué ainsi obtenu, les procédés de la composition et la mousse.