PRODUCTION METHOD FOR SHEETS OF GLASS WITH A DIFFUSE FINISH, AND RESULTING SHEET OF GLASS

The invention relates to a production method for sheets of glass with a diffuse finish, and to the sheet of glass resulting from this method. The sheet of glass is immersed in acid solutions and alkaline solutions a series of times in an alternating manner, in order to eliminate the impurities and residues, and in order to generate a diffuse finish on both faces of the sheet of glass. The method generates a diffuse surface on at least one side of the sheet of glass, said diffuse surface having a peak-valley roughness (Rt) between 5.8343 and 9.3790 µm, an average roughness (Ra) between 0.8020 and 0.9538 µm, an RMS roughness between 0.9653 and 1.19167 µm, a solar transmission between 84.8 and 46.50%, a solar reflection between 7.4 and 4.4%, a light transmission between 88.5 and 67.70%, a light reflection between 6.50 and 5.20%, and a UV transmission between 35.60 and 70.20%. La présente invention concerne un procédé de fabrication de feuilles de verre à fini diffus et la feuille de verre obtenue au moyen dudit procédé. La feuille de verre est soumise à une série d'immersions alternées dans des solutions acides et des solutions alcalines pour éliminer les impuretés et les résidus et pour produire un fini diffus sur les deux faces de la feuille de verre. Le procédé génère sur la feuille de verre au niveau d'au moins un de ses côtés, une surface diffuse ayant une rugosité de type crête-creux (Rt) comprise entre 5,8343 µm et 9.3790 µm; une rugosité moyenne (Ra) comprise entre 0,8020 µm et 0,9538 µm; une rugosité RMS comprise entre 0,9653 µm et 1.19167 µm; une transmission solaire comprise entre 84,8% et 46,50%; une réflexion solaire comprise entre 7,4 et 4,4%; une transmission de la lumière comprise entre 88,5% et 67,70%; une réflexion de la lumière comprise entre 6,50% et 5,20%; et une transmission des UV comprise entre 35,60% et 70,20%.