RECYCLABLE THERMOPLASTIC INSULATION WITH IMPROVED BREAKDOWN STRENGTH

The disclosure provides a process for producing a material with improved breakdown strength. The process includes heating a polymeric composition composed of a low density polyethylene (LDPE) and a minority amount of a high density polyethylene (HDPE). The polymeric composition is heated to at least the melting temperature of the HDPE. The process includes control-cooling the heated polymeric composition at a cooling rate from 0.1 °C/min to 20°C/min, and forming a polymeric composition. The control-cooled polymeric composition has a unique morphology which improves breakdown strength. Also provided is a coated conductor with an insulating layer composed of the polymeric composition with the unique morphology. The insulating layer exhibits improved breakdown strength. L'invention porte sur un procédé pour la production d'un matériau doté d'une résistance à la décomposition améliorée. Le procédé comprend le chauffage d'une composition polymère composée d'un polyéthylène basse densité (PE-BD) et d'une quantité mineure d'un polyéthylène haute densité (PE-HD). La composition polymère est chauffée à au moins la température de fusion du PE-HD. Le procédé comprend le refroidissement contrôlé de la composition polymère chauffée à une vitesse de refroidissement de 0,1°C/min à 20°C/min et la formation d'une composition polymère. La composition polymère refroidie de façon contrôlée a une morphologie particulière qui améliore la résistance à la décomposition. L'invention porte également sur un conducteur revêtu d'une couche isolante composée de la composition polymère présentant la morphologie particulière. La couche isolante présente une résistance à la décomposition améliorée.