ULTRA -THIN FABRIC AND MANUFACTURING METHOD

Fabric can comprise yarns comprising less than about 30 denier total and less than about 10 denier per filament; a density of greater than about 177 yarns per cm2; and a thickness of less than about 3.2 mil. The fabric can further comprise a weight of less than about 60 g/m2. The fabric can have performance characteristics equivalent to or greater than those in conventional implantable fabrics. A method of making such a fabric can include twisting together filaments into a multifilament yarn; passing adjacent yarns into a loom in parallel so as to allow the yarns to be woven together more closely; maintaining a consistent tension on the yarns during placement of the yarns on a loom beam and during weaving; and or subjecting the fabric to increased heat and pressure so as to compress the yarns more tightly. La présente invention concerne un tissu qui peut comprendre des fils qui comprennent un total inférieur à environ 30 deniers et qui comprennent moins d'environ 10 deniers par filament ; une densité supérieure à environ 177 fils par m ; et une épaisseur inférieure à environ 3,2 mil. Le tissu peut en outre posséder un poids inférieur à environ 60 g/m . Le tissu peut posséder des caractéristiques de performances équivalentes ou supérieures à celles des tissus implantables conventionnels. Un procédé de fabrication d'un tel tissu peut consister à tordre ensemble des filaments pour obtenir un fil multifilament ; à faire passer des fils adjacents dans un métier en parallèle afin de permettre aux fils d'être tissés ensemble de façon plus proche ; à maintenir une tension constante sur les fils au cours du positionnement des fils sur une ensouple de métier et au cours du tissage ; et/ou à soumettre le tissu à une chaleur et à une pression plus importantes afin de comprimer les fils de façon plus serrée.