SYNTHESIS AND USE OF ZSM-12

A process is described for synthesizing a porous, crystalline material having the framework structure of ZSM- 12 of the formula: (n)YO2: X2O3 wherein X is a trivalent element, Y is a tetravalent element and n is between about 80 and about 250. In the process, a mixture capable of forming said material is prepared comprising sources of alkali or alkaline earth metal (M), an oxide of trivalent element (X), an oxide of tetravalent element (Y), hydroxyl ions (OH'), water and tetraethylammonium cations (R), wherein said mixture has a composition, in terms of mole ratios, within the following ranges: YO2/X2O3 = 100 to 300; H2O/YO2 = 5 to 15; OH- /YO2 = 0.10 to 0.30; M/Y02 = 0.05 to 0.30; and R/YO2 = 0.10 to 0.20. The mixture is reacted at a temperature of at least about 300° F (149° C) for a time of less than about 50 hours to form crystals of the crystalline material and the crystalline material is then recovered. La présente invention a pour objet un procédé pour la synthèse d'un matériau cristallin poreux ayant la structure de la ZSM-12 de la formule : (n) YO2 : X2O3, X étant un élément trivalent, Y étant un élément tétravalent et n étant compris entre environ 80 et environ 250. Dans le procédé, un mélange capable de former ledit matériau est préparé, lequel comprend des sources de métal alcalin ou alcalino-terreux (M), un oxyde d'élément trivalent (X), un oxyde d'élément tétravalent (Y), des ions hydroxyle(OH-), de l'eau et des cations tétraéthylammonium (R), ledit mélange possédant une composition, en termes de rapports molaires, comprise dans les gammes suivantes : YO2 / X2O3 = 100 à 300 ; H2O / YO2 = 5 à 15 ; OH- / YO2 = 0,10 à 0,30 ; M / YO2 = 0,05 à 0,30 ; et R / YO2 = 0,10 à 0,20. Le mélange est mis à réagir à une température d'au moins environ 300 °F (149 °C) pendant une durée inférieure à environ 50 heures pour former des cristaux du matériau cristallin et le matériau cristallin est ensuite récupéré.