NICKEL ALLOY AND ARTICLES

Articles that include a material that has L12-structured gamma-prime phase precipitates within a matrix phase at a concentration of at least 20% by volume are disclosed. The gamma-prime phase precipitates are less than 1 micrometer in size. The material also has A3-structured eta phase precipitates distributed within the matrix phase at a concentration in the range from about 1% to about 25% by volume. The articles may be formed by mechanically working a workpiece that has at least about 40% nickel, about 1.5% to about 8% titanium, and about 1.5% to about 4.5% aluminum. The workpiece may be worked at a temperature below a solvus temperature of the eta phase; and then heat treated at a temperature sufficient to dissolve any gamma prime phase present in the workpiece but below the solvus temperature of the eta phase. Des articles qui comprennent un matériau comportant des précipités en première phase gamma de structure L12 dans une phase matricielle à une concentration dau moins 20 % par volume sont décrits. Les précipités en première phase gamma présentent une taille inférieure à 1 micromètre. Le matériau comporte également des précipités en phase eta de structure A3 répartis dans la phase matricielle à une concentration dans la plage denviron 1 % à environ 25 % par volume. Les articles peuvent être formés en travaillant mécaniquement une pièce à usiner comprenant au moins environ 40 % de nickel, environ 1,5 % à environ 8 % de titane et environ 1,5 % à environ 4,5 % daluminium. La pièce à usiner peut être travaillée à une température inférieure à une température de solvus de la phase eta, puis traitée thermiquement à une température suffisamment élevée pour dissoudre toute première phase gamma présente dans la pièce, mais inférieure à la température de solvus de la phase eta.