TUBES OF ZIRCONIUM-BASED ALLOYS AND THEIR MANUFACTURING METHOD

Tubes for use in nuclear reactors made from two zirconium base alloys: one is a binary alloy containing mainly 2.5-2.8 wt.% Nb, 0.1-0.13 wt.% O, 0.05-0.13 wt% Fe, the balance of Zr, and the other is a multicomponent alloy containing 0.9-1.2 wt.% niobium, 1.1-1.42 wt.% tin, 0.3-0.47 wt.% iron, 0.05-0.12 wt.% oxygen, the balance of zr and a method to manufacture the said tubes with such characteristics where the DHC velocity is lower than 6×10-8 m/s at 250 °C, the threshold stress intensity factor is not less than 10 MPa~m at 250 °C, fracture toughness resistance, dJ/da, is larger than 250 MPa at 250 °C and the tensile strength exceeds 480 MPa at 300 °C. On fabrique des tubes destinés à des réacteurs nucléaires à partir de deux alliages à base de zirconium : un alliage binaire renfermant principalement 2,5 à 2,8 % en poids de Nb, 0,1 à 0,13 % en poids de O, 0,05 à 0,13 % en poids de Fe, le reste étant du Zr, et l'autre alliage étant un alliage multicomposite renfermant 0,9 à 1,2 % en poids de niobium, 1,1 à 1,42 % en poids d'étain, 0,3 à 0,47 % en poids de fer, 0,05 à 0,12 % en poids d'oxygène, le reste étant du zirconium. On présente aussi une méthode pour fabriquer les tubes en question, ceux-ci ayant les caractéristiques suivantes : vitesse de fissuration différée par hydruration de 6 ž10-8 m/s à 250 degrés Celsius, seuil du facteur d'intensité de contrainte d'au moins 10 MPa m à 250 degrés Celsius, résistance à la fracturation, en dJ/da, supérieure à 250 MPa à 250 degrés Celsius, et résistance à la traction supérieure à 480 MPa à 300 degrés Celsius.