Effect of the laser shock processing on wear resistance of brass alloy

Laser shock processing (LSP) is becoming an important surface treatment to induce a compressive residual stress field, which improves micro-hardness, fatigue and fracture properties of components. In this work, we examine the effect of laser shock processing on the surface micro-hardness and wear resistance of brass alloy. After LSP treatment, micro-hardness values increased by 97 % at the metal surface and decreases gradually with distance below the surface. It is observed that LSP impact can improve the wear resistance of brass, where the wear rate is reduced by 79% compared with the untreated LSP specimens due to work hardening and compressive residual stress of LSP impact. From SEM micrograph analysis of worn surface, the grooves and compacted debris of LSP treated sample are smaller and less than these untreated LSP samples. المعاملة بواسطة موجة الصدمة المتولدة بالليزر أصبحت أكثر طرق المعاملة أهمية نضرا لما تضيفه للمادة من اجهادات انضغاط و صلادة و مقاومة الكلال و الكسر. في هذا العمل, تم اختبار تأثير المعاملة بموجة الصدمة المتولدة بالليزر على صلادة و مقاومة البلى لسبيكة البراص. بعد إجراء المعاملة بموجة الصدمة المتولدة بالليزر لسطح السبيكة, قيم الصلادة ارتفعت 97 % عند السطح و تنخفض تدريجيا كلما ابتعدنا عن السطح. تمت الملاحظة أن المعاملة بموجة الصدمة المتولدة بالليزر يمكن أن تزيد من مقاومة البلى لسبيكة البراص حيث قل معدن فقدان الكتلة بمقدار 79 % مقارنة مع العينات الغير معاملة الغير معاملة بالليزر بسبب عملية التصليد و اجهادات الانضغاط المتولدة بالسطح. تصوير المجهر الالكتروني لسطح المادة المعرض لاختبار البلى أظهر أن الاغاديد و المخلفات المنضغطة على السطح أصغر و أقل في العينات المصلدة بالليزر منها للغير مصلدة.