تأثير النيكل على كل من الطلاء ألا لوميني و مقاومة التأكسد الدوري للصلب السبائكي AISI 321

Two different types of aluminide coatings on oustenitic stainless steel 321 AISI. were investigated. One is based on prcdeposition of nickel by electrodeposition followed by aluminization using a pack cementation technique (double step-coating), while the other coating is based on codcposition of nickel and aluminium powder simultansly using a pack cementation ( single step-coating). The coating microstructure and intermetallic compound of the coating layers, as well as. coating thickness were identified using metallugraphy and X-ray analysis. The coating microstructure and intermetallic compound of the coating layers, as well as. coating thickness were identified using metallugraphy and X-ray analysis. The cyclic oxidation test of the coatings at elevated temperature reveals the formation of stable and protective scale a-AI2O3 along the exposure time. تضمن البحث دراسة بنية و أطوار الطلاء الناتج عن نوعين مختلفين من الطلاء الصلب المقاوم للصدأ من النوع الاوستنياتي 321 AISI. تضمن النوع الأول ترسيب عنصر النيكل بالطريقة الكهربائية و من ثم المنتة بطريقة بودقة السمنتة Pack cementation (طلاء المرحلتين). بينما تضمن النوع الثاني الترسيب المشترك لمسحوق مكون من عنصري النيكل و الالمنيوم بطريقة السمنتة (طلاء المرحلة الواحدة). استخدم في هذا البحث تقنية حيود الأشعة السينية X-ray diffraction و الفحص المجهري للتعرف على التركيب الدقيق و الأطوار الوسطية المتكونة فضلا عن سمك الطلاءات الناتجة و خواصها. كما أظهرت نتائج فحص الأكسدة الدورية لهذه الطلاءات في درجات الحرارة العالية، مقاومة جيدة للتأكسد بسبب تكون القشرة الاوكسيدية المستقرة و الملتحمة a-Al2O3 على مدى ساعات التعرض.