استخدام مونة السمنت المعززة بألياف الكاربون لمعالجة الأرضيات الخرسانية المعرضة للقلويات

The main purpose of this research is to repair the concrete floors in contact with alkalis action especially sodium hydroxide (caustic soda) in the floors of factories of Vegetable Oils by using cement and sand mortars incorporated with carbon fiber chips in proportions (0.5 – 1)% by volume was used ,superplasticizer with a dosage of (2 -2.6) L/100 kg cement was added, thickness of cement and sand mortars depend on damage concrete . Mechanical tests such as compressive strength test and physical tests such as ultrasonic pulse velocity , bulk density , apparent porosity and water absorption tests were done to samples after curing in normal water for ( 7 , 28 , 60 , 90 , 180 ) days and then they were exposed to caustic soda solution (37% concentration) up to six months. Test results showed a noticeable improvement in durability of suggested mortar mixes against such type of aggressive alkalis solutions. إن الهدف الأساسي من البحث هو إصلاح الأرضيات الخرسانية المتضررة بعرضها للقلويات و تحديدا مركب هيدروكسيد الصوديوم (الصودا الكاوية) في معامل الزيوت النباتية باستخدام مونة السمنت و الرمل المعززة بألياف الكربون بنسب (0,5-1)% حجما بالإضافة إلى الملدن المتفوق بجرعة (2-2,6 ) لتر / 100كغم سمنت علما بأن سمك مونة السمنت المستخدمة في المعالجة تعتمد على الجزء المتضرر. أجريت الفحوص الميكانيكية كفحص مقاومة للإنضغاط و الفحوص الفيزيائية مثل فحوص سرعة الموجات فوق الصوتية، الكثافة الكلية، النفاذية الظاهرية و امتصاص الماء للنماذج المعالجة بالماء لمدة (7، 28، 60، 90، 180) يوما و لنماذج أخرى وضعت لمدد تصل إلى ستة أشهر في محلول الصودا الكاوية بتركيز 37%. أظهرت النتائج تحسنا ملحوظا في ديمومة خلطات المونة المقترحة عند تعرضها للمحاليل القلوية القاسية.