Fracture and Fatigue of Bi-Materials

The results from several research investigations dealing with fracture and fatigue of AS1/3501-6 graphite/epoxy composite laminates are described. Investigations include static tensile fracture of laminates with a hole, crack growth of splits during tension-tension cyclic loading of unidirectional l...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
1. Verfasser:	Mar,James W
Format:	Report
Sprache:	eng
Schlagworte:	Aluminum Composite materials Composite structures Compressive properties Crack propagation Defects(Materials) Epoxy resins Fatigue life Fracture(Mechanics) Graphite Honeycomb structures Laminates Laminates and Composite Materials Mechanics Moire effects Monitoring Sandwich construction Strength(Mechanics) Tensile properties
Online-Zugang:	Volltext bestellen
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The results from several research investigations dealing with fracture and fatigue of AS1/3501-6 graphite/epoxy composite laminates are described. Investigations include static tensile fracture of laminates with a hole, crack growth of splits during tension-tension cyclic loading of unidirectional laminates with a hole, static tensile behavior of laminates with a hole, and damage initiation and propagation during compression-compression cyclic loading of a laminate with a hole. This last investigation, using Moire interferometry to detect subsurface delamination, is described.