Volume Measurements of Ferrite Magnesium Cast Iron during Heating

Volume Measurements of Ferrite Magnesium Cast Iron during Heating

The cast irons under study (C 3.0, Si 2.35, Mn 0.50, S 0.014, P 0.055, and Mg 0.063 wt. %), after graphitization annealing and specimen preparation, were tempered for 5 hr at 600 degrees and then cooled in water or with the furnace. Specimens cooled in water were tempered additionally for 5 hr at 20...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Hauptverfasser: Tkachenko,F. K, Fomina,E. G
Format: Report
Sprache:eng
Schlagworte:
ANNEALING
CAST IRON
CASTINGS
IRON
Metallurgy and Metallography
STRESSES
THERMAL EXPANSION
TRANSLATIONS
USSR
Online-Zugang:Volltext bestellen
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The cast irons under study (C 3.0, Si 2.35, Mn 0.50, S 0.014, P 0.055, and Mg 0.063 wt. %), after graphitization annealing and specimen preparation, were tempered for 5 hr at 600 degrees and then cooled in water or with the furnace. Specimens cooled in water were tempered additionally for 5 hr at 200-600 degrees at 100 degrees intervals, each time with cooling in water. After this, the dilatometric study was made and the mean coefficient of linear expansion was calculated. Unedited rough draft trans. of Izvestiya Vysshikh Uchebnykh Zavedenii. Chernaya Metallurgiya (USSR) v13 n9 p144-147 1970.