UV aged epoxy coatings ̶ Ecotoxicological effects and released compounds

•UV-A irradiated epoxy coatings led to decreased ecotoxicological effects.•UV-A irradiated epoxy coatings released toxic transformation products.•4-tert-Butylphenol was identified as main driver for ecotoxicological effects.•BPA and structural analogs contribute to estrogenic effects of irradiated materials. Organic coatings can guarantee long-term protection of steel structures due to causing a physical barrier against water and oxygen. Because of their mechanical properties and resistances to heat and chemicals, epoxy resin-based coatings are widely used for corrosion protection. Despite of the aromatic backbone and the resulting susceptibility to UV degradation, epoxy resins are frequently used as binding agent in top layers of anti-corrosion coating systems. Consequently, these organic polymers are directly exposed to sunlight and thus UV radiation. The present study was designed to investigate if toxic effects of epoxy resin-based-coatings are changed by UV-A irradiation. For this purpose, two epoxide-based top coatings were examined with and without UV aging for their bacterial toxicity and estrogenicity. In addition, chemical analyses were performed to identify released compounds as well as photolytic degradation products and to assign toxic effects to individual substances. UV-A irradiation of epoxy resin based top coatings resulted in an overall decrease of acute and specific ecotoxicological effects but as well to the formation of toxic transformation products. Both, in leachates of untreated and UV-A irradiated coatings, 4tBP was identified as the main driver of estrogenicity and toxicity to luminescent bacteria. BPA and structural analogs contributing to estrogenic effects in leachates were formed by UV-A irradiation. The combination of HPTLC coupled bioassays and LC-MS analyses supported the identification of bioactive compounds in terms of an effect-directed analysis. The present findings indicate that epoxide-based coatings are less suitable for the application as top coatings and more UV stable coatings like aliphatic polyurethanes should be preferred. [Display omitted]