Translucency and Color Stability of a Simplified Shade Nanohybrid Composite after Ultrasonic Scaling and Air-Powder Polishing

We aimed to assess the influence of professional dental prophylaxis on the translucency and color stability of a novel simplified shade nanohybrid composite material. Sixty composite disks (5 mm in diameter and 2 mm thick) of light ( = 30) and dark ( = 30) shades were prepared. The specimens were randomly divided into the following three groups ( = 10) according to the prophylaxis procedure used: ultrasonic scaling, air-powder polishing with sodium bicarbonate, and controls. The specimens were submitted to translucency and color analysis based on the CIELab system. Two measurements were performed before and after 48-h storage in coffee. Translucency values of untreated light and dark specimens were 9.15 ± 0.38 and 5.28 ± 1.10, respectively. Air-powder polishing decreased the translucency of the light composite specimens. Storage in coffee resulted in color changes (∆E) ranging between 2.69 and 12.05 and a mean translucency decrease ranging between -0.88 and -6.91. The samples in the light group tended to exhibit greater staining; the treatment method had no effect on ∆E. It can be concluded that light-shade composite restorations are more prone to translucency and color changes resulting from air-powder polishing and contact with staining media. However, further research using other composites and powders is required.