Environmental Friendly Fabrication of Porous Cement Membranes via Reusable Camphene-Based Freeze-Casting Method
Inorganic membranes have been developed rapidly in recent years because of excellent anti-fouling performance, high mechanical strength and outstanding resistances to acid and alkali. However, the high production cost still restricts its large-scale industrial application. In this work, an environme...
Gespeichert in:
Veröffentlicht in: | Membranes (Basel) 2022-09, Vol.12 (9), p.867 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Inorganic membranes have been developed rapidly in recent years because of excellent anti-fouling performance, high mechanical strength and outstanding resistances to acid and alkali. However, the high production cost still restricts its large-scale industrial application. In this work, an environmental friendly unidirectional freezing method via introducing camphene as a reusable template was adapted to prepare porous cement membranes (PCMs). The naturally formed and highly aligned porous structures of PCMs could be divided into three parts: a dense layer, a transition layer and a supporting layer. With the solid content rising from 40 wt.% to 60 wt.%, the pore size of the PCMs decreased from 3.34 nm to 3.62 nm, the bovine serum albumin (BSA) rejection increased from 81.3% to 93.5% and water flux decreased from 346.8 L·m−2·h−1 to 167.3 L·m−2·h−1 (0.2 MPa). Significantly, the performance of PCMs was maintained; even the camphene was reused 20 times. Additionally, the recovery rate of camphene could be reached up to 97.16%. Therefore, this method is cost effective and environmental friendly, which endowed the PCMs great potential in water treatment. |
---|---|
ISSN: | 2077-0375 2077-0375 |
DOI: | 10.3390/membranes12090867 |