Physico-chemical analysis of pyrolyzed bio-oil from swietenia macrophylla (mahogany) wood

The Swietenia macrophylla wood used for the study was sun dried for about 48 h, pulverized using a hammer mill and then sieved to a particle size of about 425μm using Wiley milling machine. The prepared materials were pyrolyzed in a fixed-bed pyrolysis reactor in the temperature range from 425 to 500 °C. The product yields were collected at an interval of 25 °C. The maximum yield of bio-oil was recorded as 69.5wt.% at the pyrolysis temperature of 450 °C. The physicochemical properties and compositions of the feed materials and produced bio-oil were measured in order to quantify their potential for bio-energy use and industrial applications. The properties specifically measured include density, moisture content, ash content, pH, refractive index, cetane index, elemental composition, viscosity, and heating values. The ultimate analysis of the product showed that the contents of carbon, oxygen, hydrogen, nitrogen, and sulfur were 50.2%, 42.6%, 6.6%,