Significantly Tunable Foaming Behavior of Blowing Agent for the Polyethylene Foam Resin with a Unique Designed Blowing Agent System

The chemical blowing agent plays a crucial role in enhancing the performance of the polyethylene (PE) foaming resin during the rotational foaming process. Previously, the conventional blowing agent of the PE resin commonly used pure azodicarbonamide (AZ). It had the unavoidable drawbacks of releasin...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:ACS omega 2024-02, Vol.9 (5), p.5798-5808
Hauptverfasser: Chen, Xuelian, Huang, Qigu
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The chemical blowing agent plays a crucial role in enhancing the performance of the polyethylene (PE) foaming resin during the rotational foaming process. Previously, the conventional blowing agent of the PE resin commonly used pure azodicarbonamide (AZ). It had the unavoidable drawbacks of releasing NH3 and exhibiting strong reactions during the rotational foaming process. Meantime, pure AZ had a relatively high decomposition temperature, resulting in a sharp foaming process. To address the above issues, this work developed a uniquely designed blowing agent system. In this study, a novel blowing agent for the PE resin was successfully synthesized by a one-pot method. This blowing agent consisted of an activator and AZ, which exhibited a lower decomposition temperature and a milder decomposition rate than AZ. The activator was constituted of small-sized ammonium dihydrogen phosphate on the AZ surface, which could be decomposed properly and deliver phosphoric acid and H2O during the foaming process. Then, AZ reacted with H2O under phosphoric acid catalysis. Also, this reaction generated CO2 emission while reducing the emission of NH3 through recombination with phosphoric acid. Moreover, phosphoric acid catalysis caused a decrease in the AZ decomposition temperature. Meantime, the thermal coupling appeared during the foaming process, which could further reduce the decomposition rate. Consequently, the small activator played a key role in regulating cell formation and diffusion. Compared to AZ, the novel blowing agent system significantly reduced the cell diameter of the PE foam resin and enhanced its flexural modulus by 50%. Furthermore, the novel blowing agent facilitated better demolding performance and improved the surface morphology of the PE foam product. This research provides significant foaming behavior regulation for the PE resin during industrial applications.