Structural and Tribological Studies of “(TiC + WC)/Hardened Steel” PMMC Coating Deposited by Air Pulsed Plasma

The deposition of a thin (several tens of microns) protective coating in atmospheric conditions is a challenging task for surface engineering. The structural features and tribological properties of a particle-reinforced metal matrix composite coating synthesized on middle-carbon steel by air pulse-plasma treatments were studied in the present work. The 24–31 µm thick coating of “24 vol.% (TiC + WC)/Hardened steel matrix” was produced by 10 plasma pulses generated by an electro-thermal axial plasma accelerator equipped with a consumable cathode of novel design (low-carbon steel tube filled with “TiC/WC + Epoxy resin” mixture). The study included optical microscopy (OM), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD, microhardness measurements, and dry “Ball-on-Plate” testing. The carbides were directly plasma-transferred to the substrate (steel of AISI 4145H grade) from the cathode without substantial melting. The hard (500–1044 HV) coating matrix consisted of 57 vol.% austenite (1.43 wt.% C) and 43 vol.% plate martensite was formed via carbon enrichment of steel from plasma flow. Additionally, a minor amount of oxide phases (TiO2, WO2, WO3) were dispersed in the matrix. As compared to substrate, the coating had a lower coefficient of friction; its volumetric wear was decreased by 4.4 times when sliding against hardened steel ball and by 16 times when sliding against SiC ball.