D-Alpha-Tocopheryl Poly(ethylene Glycol 1000) Succinate-Coated Manganese-Zinc Ferrite Nanomaterials for a Dual-Mode Magnetic Resonance Imaging Contrast Agent and Hyperthermia Treatments

Manganese-zinc ferrite (MZF) is known as high-performance magnetic material and has been used in many fields and development. In the biomedical applications, the biocompatible MZF formulation attracted much attention. In this study, water-soluble amphiphilic vitamin E (TPGS, d-alpha-tocopheryl poly(ethylene glycol 1000) succinate) formulated MZF nanoparticles were synthesized to serve as both a magnetic resonance imaging (MRI) contrast agent and a vehicle for creating magnetically induced hyperthermia against cancer. The MZF nanoparticles were synthesized from a metallic acetylacetonate in an organic phase and further modified with TPGS using an emulsion and solvent-evaporation method. The resulting TPGS-modified MZF nanoparticles exhibited a dual-contrast ability, with a longitudinal relaxivity (35.22 s mM Fe ) and transverse relaxivity (237.94 s mM Fe ) that were both higher than Resovist . Furthermore, the TPGS-assisted MZF formulation can be used for hyperthermia treatment to successfully suppress cell viability and tumor growth after applying an alternating current (AC) electromagnetic field at lower amplitude. Thus, the TPGS-assisted MZF theranostics can not only be applied as a potential contrast agent for MRI but also has potential for use in hyperthermia treatments.