Optimization of the Physical and Mechanical Properties of Grouting Material for Non-Soil-Squeezing PHC Pipe Pile

The physical and mechanical properties of grouting materials greatly affect the friction resistance and the bearing performance of a non-soil-squeezing PHC pipe pile. Orthogonal tests for four factors at five levels were carried out to optimize the proportion of the water–cement mixture by using Portland cement as a raw material and a water-reducing agent, expansion agent and early-strength agent as additives. The following conclusions were obtained: (1) Both the water–cement ratio and the dosage of water-reducing agent are positively correlated with the fluidity of the water–cement mixture and have the greatest influence on the fluidity, followed by the expansion agent and early-strength agent. The saturation point of the water-reducing agent is 1.5%. (2) The strength of the grouting body decreases linearly with the increase of the water–cement ratio, and the dosage of the water-reducing agent has no obvious effect on the strength. As the dosage of expansion agent increases, the strength of the grouting body decreases rapidly. The expansion agent mainly plays a key role in the middle and late stages of the hardening process of the slurry. Early-strength agents have a greater impact on the early strength, but less on the later strength. When the slurry is solidified for 3 h, the early-strength agent has the greatest impact on the strength with an optimal dosage of 5%. (3) The volume of the grouting body has an inverse relationship with the water–cement ratio, and the optimal amount of expansion agent is 12%. The incorporation of an expansion agent makes the volume increase of the grouting body exceed the volume shrinkage ratio caused by the hardening of the grouting body with a curing time of more than 3 days, ensuring a slight increase in the volume of the grouting body. After 3 days, even though the effect of the expansion agent is gradually weakened, it can still ensure that the volume of the grouting body does not shrink. With the increase of the amount of water-reducing agent, the volume of the grouting body gradually decreases. When the amount of water-reducing agent exceeds 1.5%, the volume of the grouting body no longer decreases. (4) The early-strength agent has almost no effect on the volume of the grouting body. When the curing time is 3 h, the water–cement ratio has the greatest influence on the volume of the grouting body, followed by the water-reducing agent, and, finally, the expansion agent. After 3 h, the water–cement ratio still has the g