Exploring the preparation of YbBa2Cu3O7−y superconductor in flowing oxygen atmosphere
REBCO has been used extensively as coated conductors applied to superconducting magnets due to its exceptional superconducting properties. As a REBCO superconductor, YbBa 2 Cu 3 O 7−y (Yb123) has a low melting temperature, making it suitable for use as an intermediate medium connector while preparin...
Gespeichert in:
Veröffentlicht in: | Scientific reports 2024-04, Vol.14 (1), p.8949-8949, Article 8949 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | REBCO has been used extensively as coated conductors applied to superconducting magnets due to its exceptional superconducting properties. As a REBCO superconductor, YbBa
2
Cu
3
O
7−y
(Yb123) has a low melting temperature, making it suitable for use as an intermediate medium connector while preparing the superconducting joint. However, there is still uncertainty about the formation mechanism of Yb123 and the synthesis of this superconductor has not been fully understood. Therefore, this study systematically investigated the phase transformation process of Yb123 during heat treatment in flowing oxygen. The results indicated that Yb123 sample with the highest phase purity could be obtained by annealing at 927 °C or 937 °C but not in between, respectively. Furthermore, a quantitative phase analysis revealed that the sample annealed at 937 °C had a phase purity greater than 80 wt%. Additionally, a strong c-axis texture was observed in the bulk Yb123 superconductor prepared at 937 °C. Meanwhile, the superconducting results revealed that the bulk sample’s T
c
was 89.9 K, and its self-field critical current densities at 4.2 K and 77 K were 1.3 × 10
5
A/cm
2
and 5.0 × 10
3
A/cm
2
, respectively. Based on the results mentioned above, the phase transformation process and formation mechanism of Yb123 in flowing oxygen were elaborated. |
---|---|