Research and Development of 10B38 Boron Containing Cold Heading Steel

The strength and plasticity of 10B38 boron containing cold heading steel under different high temperature condi⁃ tions were studied using high-temperature tensile testing method. The results showed that the tensile strength decreased significantly from 124. 8 MPa to 22. 9 MPa at temperatures ranging from 700 to 950 ℃； At 950 to 1 150 ℃， the tensile strength was 12. 7 to 25. 5 MPa. In terms of thermoplastic properties， the cross-sectional shrinkage rate at 700-750 ℃ was 56%-72%； When the temperature was between 800 and 1 050 ℃， the cross-sectional shrinkage rate was ≥ 75%； When the temperature was between 1 050 and 1 150 ℃， the cross-sectional shrinkage rate was greater than 65%. Based on the above experimental data， the strength of the secondary cooling water in continuous casting was optimized from a specific water content of 1. 35 L/kg to a specific water content of 1. 25 L/kg. After optimization， the crack index of the continuous casting slab was significantly reduced. The dynamic CCT curves of 10B38 boron