Hafnium-Zirconium Carbonitride (Hf,Zr)(C,N) by One Step Mechanically Induced Self-Sustaining Reaction: Powder Synthesis and Spark Plasma Sintering

Nanostructured single-phase hafnium-zirconium carbonitride powders were synthesized using a simple and fast mechanochemical synthesis approach. The critical milling duration, after which a (Hf,Zr)(C,N) solid solution formation inside a jar occurred via mechanically induced self-sustained reaction (M...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Ceramics 2023-06, Vol.6 (2), p.1129-1138
Hauptverfasser: Khadyrova, Irina, Suvorova, Veronika, Nepapushev, Andrey, Suvorov, Dmitrii, Kuskov, Kirill, Moskovskikh, Dmitry
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Nanostructured single-phase hafnium-zirconium carbonitride powders were synthesized using a simple and fast mechanochemical synthesis approach. The critical milling duration, after which a (Hf,Zr)(C,N) solid solution formation inside a jar occurred via mechanically induced self-sustained reaction (MSR), was 10 min. After 30 min of treatment, a solid-gas reaction was completed, and as a result, a homogeneous (Hf,Zr)(C,N) powder consisting of 10–500 nm submicron particles was obtained. The phase and structure evolution of the powders after different treatment durations allowed for the establishment of possible reaction mechanisms, which included the formation of Hf/Zr/C-layered composite particles, their interaction via MSR, and further grinding and nitridization. Spark plasma sintering (SPS) was used to produce bulk hafnium-zirconium carbonitride ceramics from nanostructured powder. The sample had higher values of relative density, hardness, and fracture toughness than those for binary compounds of a similar composition.
ISSN:2571-6131
2571-6131
DOI:10.3390/ceramics6020067