Preparation and Characterization of High Mechanical Strength Chitosan/Oxidized Tannic Acid Composite Film with Schiff Base and Hydrogen Bond Crosslinking

Chitosan-based composite films with good biodegradability, biocompatibility, and sustainability are extensively employed in the field of food packaging. In this study, novel chitosan/tannic acid (CTA) and chitosan/oxidized tannic acid (COTA) composite films with excellent mechanical and antibacterial properties were prepared using a tape casting method. The results showed that, when 20% tannic acid (TA) was added, the tensile strength of the CTA composite film was 80.7 MPa, which was 89.4% higher than that of the pure chitosan (CS) film. TA was oxidized to oxidized tannic acid (OTA) with laccase, and the phenolic hydroxyl groups were oxidized to an o-quinone structure. With the addition of OTA, a Schiff base reaction between the OTA and CS occurred, and a dual network structure consisting of a chemical bond and hydrogen bond was constructed, which further improved the mechanical properties. The tensile strength of 3% COTA composite film was increased by 97.2% compared to that of pure CS film. Furthermore, these CTA films with significant antibacterial effects against ( ) are likely to find uses in food packaging applications.