Effect of 9% Hydrofluoric Acid Gel Hot-Etching Surface Treatment on Shear Bond Strength of Resin Cements to Zirconia Ceramics

Background and Objectives: There is no consensus regarding the surface treatment method for achieving optimal bonding strength between zirconia and resin cements. We evaluated the effect of hot-etching with 9% hydrofluoric acid (HF) gel using the Zirconia Etchant Cloud System on zirconia surfaces and the consequent shear bond strength (SBS) of different resin cements to such surface-treated zirconia ceramics. Materials and Methods: Forty-five zirconia specimens were randomly assigned to surface-treatment groups (n = 15/group): no treatment (control, CT); sandblasting with 110-μm Al2O3 at an air pressure of 1 bar for 10 s (SB); hot-etching with 9% HF gel (HE). Post-treatment, specimens were examined using scanning electron microscopy (SEM) and surface roughness (SR) analysis. After treatment, self-adhesive resin cements (Maxcem Elite, MAZIC Cem, RelyX U200, 3M ESPE: Maplewood, MN, USA) were bonded to zirconia specimens, which were stored in distilled water at 37 °C for 24 h. All specimens were then subjected to SBS testing, using a universal testing machine, until failure. Data were analyzed using one-way analysis of variance and Tukey’s post hoc test (α = 0.05). Results: In the SEM images, roughness was greater in SB than in HE specimens. Ra and Rt values were highest in SB, followed by HE, and CT specimens. HE specimens showed significantly higher SBS values than CT or SB specimens (p < 0.05). MAZIC Cem cement, with 10-methacryloyloxydcyl dihydrogen phosphate yielded the highest SBS values. Conclusions: Hot-etching with 9% HF gel in a safe shell formed uniformly small, defined holes on the zirconia surface and achieved significantly higher SBS values than sandblasting (p < 0.05). Zirconia prostheses can be bonded micromechanically with resin cement, without the deterioration of properties due to t-m transformation, using chemical acid etching with the Zirconia Etchant Cloud System.