Geopolimeros com base em cinzas volantes activadas com naoh y Ca(OH)2: caracterização microestrutural por rmn-mas 29Si y 27Al

In fly-ash alkali-activation technology, depending on the combination of activators, deleterious reactions may result in a drop in resistance with age. This Studiy aimed to evaluate the compressive strength of alkali-activated fly ash from combined solutions of NaOH and Ca(OH)2. Three molar ratio CaO/SiO2 (C/S) were studied: 0.05 (M5), 0.15 (M15) e 0.25 (M25). Resistances order of 21 MPa (M15) and 19 MPa (M25) were reached at the age of 7 days. However, after 28 and 91 days, the resistances were 8 MPa and 7 MPa, respectively. The M5 samples showed rising behavior of resistance with age. Thus, the drop in resistance has conditioned the C/S matrices. In the 29Si NMR spectra of the M25 sample Si has decreased species Q4 (3Al) and Q4 (2Al), those responsible for the mechanical properties of activated samples. Na tecnologia de álcali-ativação de cinzas volantes, dependendo da combinação dos ativadores, reações deletérias poderão resultar em queda na resistência com a idade. Assim, este trabalho teve como objetivo avaliar a resistência à compressão de cinzas volantes álcali-ativadas,a partir de soluções combinadas de NaOH e Ca(OH)2. Três relações molares CaO/SiO2 (C/S) foram estudadas: 0.05 (M5), 0.15 (M15) e 0.25 (M25). Resistências da ordem de 21 MPa (M15) e 19 MPa (M25) foram atingidas na idade de 7 dias. Porém, aos 28 e 91 dias as resistências foram de 8 MPa e 7 MPa, respetivamente. As amostras M5 apresentaramcomportamento ascendente da resistência com a idade. Assim, a queda na resistência está condicionada a relação C/S das matrizes. Nos espectros 29Si RMN da amostra M25 o Si apresenta diminuição das espécies Q4(3Al) e Q4(2Al), estes responsáveis pelas características mecânicas das amostras ativadas.