Crystallization kinetics of K2O·TiO2·3GeO2 glass studied by DTA

Crystallization kinetics of K2O?TiO2?3GeO2 glass was investigated by differential thermal analysis (DTA). Experiments were performed on powder samples with a particle size < 0.037 mm. The glass samples were heated at different rates in the temperature range 20-750?C. The kinetic parameters, activ...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Science of sintering 2008, Vol.40 (3), p.333-338
Hauptverfasser: Grujic, S., Blagojevic, N., Tosic, M., Zivanovic, V., Nikolic, J.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Crystallization kinetics of K2O?TiO2?3GeO2 glass was investigated by differential thermal analysis (DTA). Experiments were performed on powder samples with a particle size < 0.037 mm. The glass samples were heated at different rates in the temperature range 20-750?C. The kinetic parameters, activation energy for the crystallization process, Ec and Avrami exponent, n were calculated. Powder X-ray diffraction analysis (XRD) of crystallized glass reveals the presence of crystalline K2O?TiO2?3GeO2 indicating polymorphic crystallization with interface controlled crystal growth. Kinetika kristalizacije K2O?TiO2?3GeO2 stakla je proucavana primenom diferencijalno termijske analize (DTA). Eksperimenti su izvedeni na uzorcima stakla granulacije
ISSN:0350-820X
1820-7413
DOI:10.2298/SOS0803333G