Thermal Properties of Ethanol Organosolv Lignin Depending on Its Structure

In general, lignin exhibits unpredictable and nonuniform thermal properties due to the structural variations caused by the extraction processes. Therefore, a systematic understanding of the correlation between the extraction conditions, structural characteristics, and properties is indispensable for...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:ACS omega 2021-01, Vol.6 (2), p.1534-1546
Hauptverfasser: Choi, June-Ho, Cho, Seong-Min, Kim, Jong-Chan, Park, Sang-Woo, Cho, Young-Min, Koo, Bonwook, Kwak, Hyo Won, Choi, In-Gyu
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In general, lignin exhibits unpredictable and nonuniform thermal properties due to the structural variations caused by the extraction processes. Therefore, a systematic understanding of the correlation between the extraction conditions, structural characteristics, and properties is indispensable for the commercial utilization of lignin. In this study, the effect of extraction conditions on the structural characteristics of ethanol organosolv lignin (EOL) was investigated by response surface methodology. The structural characteristics of EOL (molecular weight, hydroxyl content, and intramolecular coupling structure) were significantly affected by the extraction conditions (temperature, sulfuric acid concentration, and ethanol concentration). In addition, the correlation between the structural characteristics and thermal properties of the extracted EOLs was estimated. The relevant correlations between the structural characteristics and thermal properties were determined. In particular, EOLs that had a low molecular weight, high phenolic hydroxyl content, and low aryl–ether linkage content exhibited prominent thermal properties in terms of their initial decomposition rate and a high glass transition temperature, T g. Correspondingly, EOL-PLA blends prepared using three EOL types exhibited improved thermal properties (starting point of thermal decomposition and maximum decomposition temperature) compared to neat PLA and had thermal decomposition behaviors coincident with the thermal properties of the constituent EOLs.
ISSN:2470-1343
2470-1343
DOI:10.1021/acsomega.0c05234