Preparation and Characterization of Asphalt Pitch-Derived Activated Carbons with Enhanced Electrochemical Performance as EDLC Electrode Materials
This study used a physical activation method to prepare asphalt-pitch-derived activated carbon (Pitch AC) for an electric double-layer capacitor (EDLC) electrode. X-ray diffraction analysis and Raman spectroscopy were used to estimate the change in the crystal structure of Pitch AC with activation t...
Gespeichert in:
Veröffentlicht in: | Minerals (Basel) 2023-06, Vol.13 (6), p.802 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | This study used a physical activation method to prepare asphalt-pitch-derived activated carbon (Pitch AC) for an electric double-layer capacitor (EDLC) electrode. X-ray diffraction analysis and Raman spectroscopy were used to estimate the change in the crystal structure of Pitch AC with activation time. In addition, the textural properties of Pitch AC were studied by Brunauer-Emmett-Teller (BET), Dubinin-Radushkevich (DR) and non-localized density functional theory (NLDFT) equations with N2/77K isotherm adsorption-desorption curves. The electrochemical performance of the Pitch AC was analyzed using a coin-type EDLC with 1 M SBPBF4/PC via galvanostatic charge/discharge, cyclic voltammetry and electrochemical impedance spectroscopy. The specific surface area and total pore volume were 990–2040 m2/g and 0.42–1.51 cm3/g, respectively. The pore characteristics of the Pitch AC varied according to the activation time and changed from a microporous structure to a micro-mesoporous structure as the activation time increased. The electrochemical performance analysis also found that the specific capacity was increased from 43.6 F/g to 84.5 F/g at 0.1 A/g as activation time increased. In particular, Pitch AC-9 exhibited the best electrochemical performance (rectangular CV curve, reversible GCD, lowest ion charge transfer resistance and Warburg impedance). In addition, Pitch AC-9 was confirmed to have a specific capacitance similar to commercial activated carbon for EDLC (YP-50F). Therefore, it was considered that Pitch AC could replace commercial activated carbon for EDLC because it has excellent pore characteristics and electrochemical performance despite being manufactured through a very low-cost precursor and a simple process (physical activation method). |
---|---|
ISSN: | 2075-163X 2075-163X |
DOI: | 10.3390/min13060802 |