The Atomic Layer Etching Technique with Surface Treatment Function for InAlN/GaN Heterostructure
This paper studied an atomic layer etching (ALE) technique with a surface treatment function for InAlN/GaN heterostructures with AlN spacer layers. Various parameters were attempted, and 30 s O2 + 15 W BCl3 was chosen as the optimal recipe. The optimal ALE approach exhibited satisfactory etching res...
Gespeichert in:
Veröffentlicht in: | Crystals (Basel) 2022-05, Vol.12 (5), p.722 |
---|---|
Hauptverfasser: | , , , , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | This paper studied an atomic layer etching (ALE) technique with a surface treatment function for InAlN/GaN heterostructures with AlN spacer layers. Various parameters were attempted, and 30 s O2 + 15 W BCl3 was chosen as the optimal recipe. The optimal ALE approach exhibited satisfactory etching results, with regard to the etch-stop effect, compared with other techniques. The atomic force microscopy (AFM) results showed an etching per cycle (EPC) value of 0.15 nm/cycle, with a 0.996 fit coefficient and root mean square (RMS) surface roughness of around 0.61 nm (0.71 nm for as-grown sample), which was the lowest in comparison with digital etching (0.69 nm), Cl2/BCl3 continuous etching (0.91 nm) and BCl3 continuous etching (0.89 nm). X-ray photoelectron spectroscopy (XPS) and scanning transmission electron microscopy with energy dispersive X-ray spectroscopy measurements (STEM/EDS) verified the indium clustered phenomena at the bottom apex of V-pit defects in the epi structure of InAlN/GaN high electron mobility transistors (HEMTs) for the first time, in addition to the surface morphology optimization for the ALE under-etching technique used in this work. The resistor hall effect (Hall) and AFM measurements demonstrated that after 4 or 5 ALE cycles, the two-dimensional electron gas (2-DEG) density and RMS roughness were improved by 15% and 11.4%, respectively, while the sheet resistance (Rsh) was reduced by 6.7%, suggesting a good surface treatment function. These findings were important for realizing high-performance InAlN/GaN HEMTs. |
---|---|
ISSN: | 2073-4352 2073-4352 |
DOI: | 10.3390/cryst12050722 |