Study of Nitridation Effect on Structural, Morphological, and Optical Properties of GaAs Film Growth on Silicon Substrates via Close Space Vapor Transport Technique

In this work, Gallium Arsenide (GaAs) films growth via Close Space Vapor Transport (CSVT) technique on n-type Silicon (Si) substrates (100) and its nitridation effect in the ammonia (NH3) environment is reported. The GaAs films were grown at 800, 900, and 1000 ∘C, and the nitridation process was car...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Crystals (Basel) 2023-04, Vol.13 (4), p.613
Hauptverfasser: Valdez-Torija, Eduardo Alejandro, Coyopol, Antonio, García-Salgado, Godofredo, Romano-Trujillo, Román, Morales-Ruiz, Crisóforo, Rosendo-Andrés, Enrique, Vásquez-Agustín, Marco Antonio, Gracia-Jiménez, Justo Miguel, Galeazzi-Isasmendi, Reina, Morales-Morales, Francisco
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this work, Gallium Arsenide (GaAs) films growth via Close Space Vapor Transport (CSVT) technique on n-type Silicon (Si) substrates (100) and its nitridation effect in the ammonia (NH3) environment is reported. The GaAs films were grown at 800, 900, and 1000 ∘C, and the nitridation process was carried out at 900 ∘C with an NH3:H2 gasses ratio. The GaAs films with and without nitridation process were analyzed using X-ray diffraction (XRD), Raman spectroscopy, Diffuse Reflectance Spectroscopy, and Scanning Electron Microscopy with Energy Dispersive X-ray analysis (SEM-EDX). Grazing incidence X-ray diffraction measurements of GaAs films nitrided confirm a polycrystalline GaN wurtzite structure with preferential orientation along (002), and additionality, a crystallographic plane (310) of low intensity is observed in 2θ=52.18∘ corresponding to Ga2O3. The average quantification results in weight (Wt. %) of GaAs films nitrided was determined by EDS; Ga∼79, N∼17.1, O∼2 and As∼1.8 Wt. %. The presence of GaN, GaxOy, Si, and GaAs modes were found by Raman measurements, demonstrating a partial nitriding. The band gap estimation by diffuse reflectance was between 3.2 and 3.38 eV such values are close to that reported for bulk GaN (3.4 eV). The presence of oxygen in the structure could be related to substrates or the GaAs source.