Influence of Heat Treatment on Fracture Toughness and Wear Resistance of Nicral-Zro2 Multilayered Thermal Barrier Coating

The chemical composition and fracture toughness of thermal barrier coatings (TBCs) before and after heat treatment were characterized, and the cracks around the interface between the coating and the substrate could be successfully eliminated and meanwhile the porosity of the coatings tended to reduce. The XRD analysis revealed the coatings were composed of non-transformable tetragonal t’ phase of ZrO and -(Ni, Cr) with minor Ni3Al ( ) precipitates. Additionally, the relationship between the heat treatment and wear resistance was systematically studied. The results indicated that both the hardness and fracture toughness increased after quenching process. The oxidation wear became more prominent after heat treatment, which probably resulted from the better bonding strength of coatings. Dense and homogeneous microstructure introduced by vacuum oil-quenching improved stabilization of the weight gain during thermal cycle test.