Effects of Ultrasonic Impact Treatment on the Stress-Controlled Fatigue Performance of Additively Manufactured DMLS Ti-6Al-4V Alloy

Additive manufacturing (AM) offers many advantages for the mechanical design of metal components. However, the benefits of AM are offset to a certain extent by the poor surface finish and high residual stresses resulting from the printing process, which consequently compromise the mechanical propert...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Applied sciences 2019-11, Vol.9 (22), p.4787
Hauptverfasser: Walker, Peter, Malz, Sinah, Trudel, Eric, Nosir, Shaza, ElSayed, Mostafa S.A., Kok, Leo
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Additive manufacturing (AM) offers many advantages for the mechanical design of metal components. However, the benefits of AM are offset to a certain extent by the poor surface finish and high residual stresses resulting from the printing process, which consequently compromise the mechanical properties of the parts, particularly their fatigue performance. Ultrasonic impact treatment (UIT) is a surface modification process which is often used to increase the fatigue life of welds in ship hulls and steel bridges. This paper studies the effect of UIT on the fatigue life of Ti-6Al-4V manufactured by Direct Metal Laser Sintering (DMLS). The surface properties before and after the UIT are characterized by surface porosity, roughness, hardness and residual stresses. Results show that UIT enhances the fatigue life of DMLS Ti-6Al-4V parts by suppressing the surface defects originating from the DMLS process and inducing compressive residual stresses at the surface. At the adopted UIT application parameters, the treatment improved the fatigue performance by 200%, significantly decreased surface porosity, reduced the surface roughness by 69%, and imposed a compressive hydrostatic stress of 1644 MPa at the surface.
ISSN:2076-3417
2076-3417
DOI:10.3390/app9224787