Fabrication and characterization of highly pure and fine copper powder by electrodeposition

Electrode position is a candidate method for producing fine and pure copper powder, which have a wide range of uses in different fields such as in applications of aerospace, atomic energy, defense, electronics^ paints, plastics, cutting tools, ...etc. This work focusing on studying some working variables such as voltage, temperature, copper sulfate concentration, sulfuric acid concentration, circulation velocity and lanoline addition on fineness andproducebiiity of deposited copper powder. Optimum conditions concluded for copper powder fineness were at (1.6V, 30 °C, 25g / L of copper sulfate, J50g / L of sulfuric acid and circulation velocity of 150 rpm. Addition of 0.075 g of lanoline increase the fineness of deposited copper powder, but did not affect clearly the dendritic shape of deposited particles. يعتبر الترسيب الكهربائي من الطرق الواعدة في مجال تحضير و إنتاج مسحوق نحاس ناعم و نقي و الذي بدوره يستخدم و بشكل واسع في مجالات عديدة مثل التطبيقات الفضائية و الطاقة الذرية و الدفاعية و الإلكترونية و الأصباغ و البلاستيك و عدد القطع ...الخ. يركز هذا العمل على دراسة بعض المتغيرات التشغيلية مثل الفولتيه و درجة الحرارة و تركيز كبريتات النحاس و حامض الكبريتيك و سرعة تدوير محلول الخلية الألكتروليتي و إضافة مادة اللانولين على نعومة و كمية مسحوق النحاس المترسب. الظروف المثلى المستحصلة من هذه الدراسة لتحضير مسحوق نحاس عالي النعومة كانت عند (1.6 V، 30 °م، 25 غم / لتر كبريتات النحاس، 150 غم / لتر حامض الكبريتيك و سرعة تدوير المحلول الألكتروليتي 150 دورة / دقيقة. و بينت الدراسة أن إضافة 0.075 غم / لتر من مادة اللانولين أدت إلى زيادة نعومة المسحوق المترسب و لكن إضافة هذه المادة لم تؤثر و بشكل واضح على شكل الدقائق الشجيري لمسحوق النحاس المترسب.