Microstructure and mechanical properties of friction stir welded 8 mm pipe SAF 2507 super duplex stainless steel

Microstructure and mechanical properties of friction stir welded 8 mm pipe SAF 2507 super duplex stainless steel

The microstructure and mechanical properties of 8-mm-thick friction stir welded SAF 2507 super duplex stainless steel pipe was examined. High-quality welds were successfully produced using polycrystalline cubic boron nitride (PCBN) tool, force control mode of 38 kN, travel speed of 50 mm/min, rotati...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials research and technology 2019-01, Vol.8 (1), p.243-249
Hauptverfasser: Giorjão, Rafael Arthur Reghine, Pereira, Victor Ferrinho, Terada, Maysa, Fonseca, Eduardo Bertoni da, Marinho, Ricardo Reppold, Garcia, Diego Martins, Tschiptschin, André Paulo
Format: Artikel
Sprache:eng
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The microstructure and mechanical properties of 8-mm-thick friction stir welded SAF 2507 super duplex stainless steel pipe was examined. High-quality welds were successfully produced using polycrystalline cubic boron nitride (PCBN) tool, force control mode of 38 kN, travel speed of 50 mm/min, rotational speed of 200 rpm. Hardness and tensile tests were performed, showing hardness increase in the stir zone and failure on the base metal. Thermal simulation showed maximum global temperatures around 1176 °C, and different thermal cycles along the joint thickness, providing microstructural and mechanical differences along the welded joint. Keywords: Friction stir welding, 2507 SDSS, Thermal simulation
ISSN:2238-7854
DOI:10.1016/j.jmrt.2018.01.002