Kirkendall Effect in Twin-Roll Cast AA 3003 Aluminum Alloy

The formation of an inhomogeneous structure with central segregation occurs in commercial twin-roll cast AA 3003 aluminum alloy. The segregations form as manganese, iron, and silicon-rich channels spread in the rolling direction. Diffusion of silicon occurs during annealing at 450 °C, and the format...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Crystals (Basel) 2022-05, Vol.12 (5), p.607
Hauptverfasser: Bajer, Jan, Zaunschirm, Stefan, Plank, Bernhard, Šlapáková, Michaela, Bajtošová, Lucia, Cieslar, Miroslav, Kastner, Johann
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The formation of an inhomogeneous structure with central segregation occurs in commercial twin-roll cast AA 3003 aluminum alloy. The segregations form as manganese, iron, and silicon-rich channels spread in the rolling direction. Diffusion of silicon occurs during annealing at 450 °C, and the formation and growth of voids due to the Kirkendall effect occur. The evolution of pores studied by scanning electron microscopy and X-ray computed tomography shows that pores are formed near original pure silicon clusters. Their coalescence and the formation of large voids in the central zone of the strip occur at longer annealing times.
ISSN:2073-4352
2073-4352
DOI:10.3390/cryst12050607