Peroxide curing systems applied for cross-linking of rubber compounds based on SBR

The work was aimed at the investigation of influence of peroxide curing system on cross-linking and properties of rubber compounds based on SBR. First, the temperature of vulcanization and the amount of dicumyl peroxide on curing process and physical-mechanical properties were investigated. Then, co-agents Type I and Type II were added to the rubber formulations cured with peroxide. The results revealed that the increase in temperature leads to the acceleration of curing process while both, curing kinetics and physical-mechanical properties were influenced by the amount of peroxide. The application of Type I co-agents resulted in the acceleration of curing process and increase in cross-link density of vulcanizates, which was reflected in the increase of hardness and decrease of elongation at break. The influence of Type II co-agents on curing kinetics was negligible, while most of them caused the reduction in cross-linking degree of vulcanizates. Type I co-agents contributed to the improvement of tensile strength of vulcanizates, while the influence of Type II co-agents on tensile strength was of minor importance.