A novel biomimetic nanofibrous cardiac tissue engineering scaffold with adjustable mechanical and electrical properties based on poly(glycerol sebacate) and polyaniline

Biomaterial tissue engineering scaffolds play a critical role in providing mechanical support, promoting cells growth and proliferation. However, due to the insulation and inappropriate stiffness of most biomaterials, there is an unmet need to engineer a biomimetic nanofibrous cardiac tissue engineering scaffold with tailorable mechanical and electrical properties. Here, we demonstrate for the first time the feasibility to generate a novel type of biocompatible fibrous scaffolds by blending elastic poly(glycerol sebacate) (PGS) and conductive polyaniline (PANI) with the help of a nontoxic carrier polymer, poly (vinyl alcohol) (PVA). Aligned and random PGS/PANI scaffolds are successfully obtained after electrospinning, cross-linking, water and ethanol wash. Incorporating of different concentrations of PANI into PGS fibers, the fibrous sheets show enhanced conductivity and slower degradation rates while maintaining the favorable hemocompatibility. The elastic modulus of the PGS/PANI scaffolds is in the range of 0.65–2.18 MPa under wet conditions, which is similar to that of natural myocardium. All of these fibrous mats show good cell viability and were able to promote adhesion and proliferation of H9c2 cells. Furthermore, the in vivo host responses of both random and aligned scaffolds confirm their good biocompatibility. Therefore, these PGS/PANI scaffolds have great potential for cardiac tissue engineering. [Display omitted] •A novel cardiac tissue engineering scaffold with adjustable mechanical and electrical properties was fabricated.•The PGS/PANI composite scaffolds showed satisfactory electroactivity, good biocompatibility, and fatigue resistance.•The aligned fibrous structure of PGS/PANI mats significantly promoted cellular elongation and alignment.•Substantial cell infiltration and collagen deposition could be observed in the fibrous composite scaffolds.